Sample

LOCTITE® HHD 3542

Hi-PURSHOT 8958

3M 2710p

Weldbond 7035E

EH9650WM

VH-818

VH-820

Viscosity,Brookfield -
Thermosel,Spindle 27

5500mpa.s
100°C

6000mpa.s
110°C

6500mpa.s
110°C

6500mpa.s100°C

5500mpa.s
100°C

7000mpa.s
110°C

6000mpa.s
110°C

Elongaion at break ISO
527-2, %

860

1300

770

770

600

700

1100

Open time@ 25 °C, minutes,
1 mm bead <4

4

2

3

4

4

2

4

Application temperature/°C

90-110

100-120

110-120

105-125

100-115

100-120

100-120

Shear strength
(PC/PC),/Cured for 7 days @
25°C PSI

870

860

885

962

890

890

850

Shear strength(Anodised
Aluminum ),Cured for 7
days @ 25°C PSI

780

780

450

548

690

780

1080

Shore Hardness, ISO 868,
Durometer D

30

28

37

29

30

30

28