Introduction
304L stainless steel is a kind of general low carbon stainless steel, it is widely used to make for a good comprehensive performance, corrosion resistance ,form-ability of equipment and parts.

It has corrosion resistance and good heat resistance, low temperature resistance and good mechanical properties. No heat treatment hardening phenomenon (non-magnetic, using temperature to -196 ℃ ~ 800 ℃).

Applied to the grain boundary corrosion resistant requirements of high chemical industry, coal, oil field open machine, building materials with heat-resistant parts and heat treatment which are difficult parts.

Technical Parameter

304L stainless steel
Standard	Grade	Chemical Composition %	Temper	Yied strength Mpa	Tensile strength Mpa	Elongation %	Hardness
GB	00Cr19Ni10	C≤0.030，Mn≤2.00， Si≤1.00，P≤0.045， S≤0.030，Cr 18.0~20.0, Ni 8~12	Annealed, hot rolled	≥170	≥480	≥40	HV≤200
USA	304L
JIS	SUS304L
German	1.4306

Specification	3.0mm*100mm
	Width:500-2000mm normal size1000 1219 1250 1500
	Length:1000-6000mm normal size 3000 6000mm
Mill	TISCO BAOSTEEL LISCO BAOXIN ZPSS JISCO
Finish	No.1
Edge	Mill /raw or slit edge
Weight	ThicknessXWidthXLengthX7.93 per sheet
Technique	hot rolled
Payment term	30% T/T in advance,the balance before shipment 30% T/T in advance,the balance L/C at sight 100% L/C at sight
Packing	1.Export sea worthy package + water proof paper + wooden pallet 2.Max Loading 25mt for each 20GP container 3.Safe loading and fixing Professional Teams
Delivery time	Within 7-10 working days after received 30%T/T of deposit or L/C original
Trade terms	FOB SHANGHAI CFR&CIF your port
Quality control	Mill Test Certificate is supplied with shipment
Application	1.Construction field, shipping building industry 2. Petroleum and Chemical Industries 3.Food and Mechanical Industries

Hot-rolled plate
1. Toughness and poor surface roughness, the price is low;
2. The temperature of hot rolling is similar to the forging temperature;
3. Hot plate with hot rolling surface oxide processing, thickness difference
4. Hot-rolled product prices and the use of relatively cold to a wide range of more;
5. Hot-rolled steel, mechanical properties far less than cold, but also inferior to forging processing, but have good toughness and ductility
6. The surface of the hot-rolled plate without plating is dark brown
7. From the plating can be distinguished from the degree of surface smoothness, hot rolled plate smoothness is low.

Application
304L,It belongs to the Austenitic steel,which is applied to the grain boundary corrosion resistant requirements of high chemical industry, coal, oil field open machine, building materials with heat-resistant parts and heat treatment which are difficult parts.