316Ti (UNS S31635) is a titanium stabilised version of 316 molybdenum-bearing austenitic stainless steel. The 316 alloys are more resistant to general corrosion and pitting/crevice corrosion than the conventional chromium-nickel austenitic stainless steels such as 304. They also offer higher creep, stress-rupture and tensile strength at elevated temperature. High carbon Alloy 316 stainless steel can be susceptible to sensitisation, the formation of grain boundary chromium carbides at temperatures between approximately 900 and 1500°F (425 to 815°C) which can result in intergranular corrosion. Resistance to sensitisation is achieved in Alloy 316Ti with titanium additions to stabilise the structure against chromium carbide precipitation, which is the source of sensitisation. This stabilisation is achieved by an intermediate temperature heat treatment, during which the titanium reacts with carbon to form titanium carbides. This significantly reduces susceptibility to sensitisation in service by limiting the formation of chromium carbides. Thus, the alloy can be used for extended periods at elevated temperatures without compromising its corrosion resistance. 316Ti has equvilent corrosion resistance to sensitisation as the low carbon version 316L.

STANDARDS
INDUSTEEL TRADEMARKS		UNS	ASTM	EURONORMS EN	SUS
316Ti		S31635	316Ti	1.4571 X6CrNiMoTi17-12-2	SUS 316Ti
CHEMICAL ANALYSIS (%WEIGHT)
C	Cr	Ni	Mo	N	Others
< 0,080	17	11	2,1	-	Ti ≥ 5 x (C+N)

PROPERTIES
0,2 Y.S. - Rp 0,2min ASTM / EN		0,2 Y.S. - Rp 0,2(2)typical value		UTS - Rm min ASTM / EN		UTS - Rm(2)typical value		EI-A(1)%	PREN(4)	HOMOLOGATIONS
MPa	Ksi	MPa	Ksi	MPa	Ksi	MPa	Ksi			Last revised
220	32	275	40	520	75	560	81	40	24

Standard	ASTM, AISI, ASME, JIS, SUS, DIN, EN, GB, BS
specification	1000mm*2000mm 1219mm* 2438mm or as your requirement
Surface	2B/cold rolled, hot rolled, hairline, mirror
type	Sheet/Plate, Pipe/Tube, Bar/rod, wire, coil, fitting etc
Thickness	0.3mm~50mm or as your requirement
Usage	Plate heat exchanger, bellows, household goods (1, 2 tableware,  cabinets, indoor pipes, water heaters, boilers, bath), auto parts (windshield wipers, muffler, moldings), medical equipment, building materials, chemical, food industry , agriculture, ship parts, and so on.
We can customize the size you need, please feel free to contact us!

APPLICATIONS
CHEMICAL INDUSTRIES			PROCESS INDUSTRIES			WATER TREATMENT			STORAGE & TRANSPORTATION
Nitric Acid	Sulfuric Acid	Polymer& otheracids	Fertilisers	Pulp& Paper	Hydrome-tallurgy	Seawater& desalination	Freshwater &Tanks	Waste Water	Chemical Tanks	Cryogenic Tanks	Renewable

POWER GENERATION				OIL & GAS			CONSTRUCTION
Nuclear	Pollution control	Hydroelectric	Renewable	Off & Onshore & production	Refining & Gas processing	Petrochemical	Architecture	Bridges

For more technical details :
(1) Indicative typical values
(2) Indicative typical values for thickness 20 mm at RT for transverse direction
(3) Hardening 496°C (925°F), 4h, air cooling
(4) PREN = Cr + 3.3 Mo + 16N
(5) PRENW = Cr + 3.3(Mo + 0.5W) + 16N
(6) HT: mechanical properties depend on heat treatment