Stainless steel grade 304N is the most commonly used stainless steel. Stainless steel grade 304N has better corrosion resistance than grade 302, and is mostly non-magnetic in nature; however when cold worked it acquires a slightly magnetic quality.

STANDARDS
INDUSTEEL TRADEMARKS		UNS	ASTM	EURONORMS EN	SUS
304N		S30451	304N	1.4315 X5CrNiN19-9	SUS 304N1
CHEMICAL ANALYSIS (%WEIGHT)
C	Cr	Ni	Mo	N	Others
< 0,080	18,5	8,5	-	0,17

PROPERTIES
0,2 Y.S. - Rp 0,2min ASTM / EN		0,2 Y.S. - Rp 0,2(2)typical value		UTS - Rm min ASTM / EN		UTS - Rm(2)typical value		EI-A(1)%	PREN(4)	HOMOLOGATIONS
MPa	Ksi	MPa	Ksi	MPa	Ksi	MPa	Ksi			Last revised
270	39	350	51	550	80	610	88	40	21

APPLICATIONS
CHEMICAL INDUSTRIES			PROCESS INDUSTRIES			WATER TREATMENT			STORAGE & TRANSPORTATION
Nitric Acid	Sulfuric Acid	Polymer& otheracids	Fertilisers	Pulp& Paper	Hydrome-tallurgy	Seawater& desalination	Freshwater &Tanks	Waste Water	Chemical Tanks	Cryogenic Tanks	Renewable

POWER GENERATION				OIL & GAS			CONSTRUCTION
Nuclear	Pollution control	Hydroelectric	Renewable	Off & Onshore & production	Refining & Gas processing	Petrochemical	Architecture	Bridges

For more technical details :
(1) Indicative typical values
(2) Indicative typical values for thickness 20 mm at RT for transverse direction
(3) Hardening 496°C (925°F), 4h, air cooling
(4) PREN = Cr + 3.3 Mo + 16N
(5) PRENW = Cr + 3.3(Mo + 0.5W) + 16N
(6) HT: mechanical properties depend on heat treatment